Method to improve mechanical strength of low-K dielectric film using modulated UV exposure

ABSTRACT

Methods and apparatus for improving mechanical properties of a dielectric film on a substrate are provided. In some embodiments, the dielectric film is a carbon-doped oxide (CDO). The methods involve the use of modulated ultraviolet radiation to increase the mechanical strength while limiting shrinkage and limiting any increases in the dielectric constant of the film. Methods improve film hardness, modulus and cohesive strength, which provide better integration capability and improved performance in the subsequent device fabrication procedures such as chemical mechanical polishing (CMP) and packaging.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of and claims priority to U.S. patent application Ser. No. 12/566,514, filed Sep. 24, 2009, titled “Method To Improve Mechanical Strength Of Low-K Dielectric Film Using Modulated UV Exposure,” which is a continuation of U.S. application Ser. No. 11/824,049, now U.S. Pat. No. 7,611,757, filed Jun. 28, 2007, titled “Method To Improve Mechanical Strength Of Low-K Dielectric Film Using Modulated UV Exposure,” which is a continuation of U.S. patent application Ser. No. 10/825,888 filed on Apr. 16, 2004, now issued U.S. Pat. No. 7,253,125, titled “Method To Improve Mechanical Strength Of Low-K Dielectric Film Using Modulated UV Exposure,” all of which are incorporated herein by reference in their entireties.

The following patent applications are incorporated by reference in their entireties and for all purposes: U.S. patent application Ser. No. 10/800,377, filed on Mar. 11, 2004, titled “Method and Apparatus for UV Exposure of Porous Low-k Films for Porogen Removal and Film Hardening,” by Cho et al; U.S. patent application Ser. No. 10/807,680, filed on Mar. 23, 2004, titled “Methods of Porogen Removal for Porous Low Dielectric Constant Films Using Plasma Treatments,” by Wu et al.; U.S. patent application Ser. No. 10/672,311, filed on Sep. 26, 2003, titled “Method of Porogen Removal from Porous Low-k Films Using UV Radiation,” by Tipton et al.; and U.S. patent application Ser. No. 10/404,693, filed on Mar. 31, 2003, titled “Method for Forming Porous Films by Porogen Removal Combined with In Situ Surface Modification,” by Humayun et al.

BACKGROUND

This invention relates to methods and apparatus for preparing dielectric films for integrated circuits, particularly carbon-doped oxide (CDO) dielectric films. More specifically, the invention employs modulated ultraviolet radiation to increase the hardness and modulus of the film. In preferred embodiments, the film shrinkage and dielectric constant are minimally affected.

Modern integrated circuit manufacturing requires advanced techniques for creating materials having low dielectric constants (low-k materials). Using low-k materials as the inter-metal and/or inter-layer dielectric in integrated circuits reduces the delay in signal propagation due to capacitive effects. The lower the dielectric constant of the dielectric film, the lower the capacitance of the dielectric and the lower the RC delay of the integrated circuit (IC).

Low k dielectrics are conventionally defined as those materials that have a dielectric constant lower than that of silicon dioxide, that is k<4. However, with ever increasing technology demands, present efforts are focused on developing low-k dielectric materials with k less than 2.5. Methods of obtaining these ultra low-k materials include doping silicon dioxide with carbon to create a carbon-doped oxide (CDO), or incorporating air voids within a low-k dielectric to create a porous dielectric material, or a combination of both (i.e., creating a CDO porous dielectric).

Although these approaches of doping and/or introducing air voids into the dielectric will reduce the dielectric constant of films, they can also have detrimental effects on quality of the films, in particular the mechanical strength of the films. Introducing carbon (e.g., methyl groups) or air voids into the dielectric will reduce the density of the film and thereby reduces the mechanical strength of the films. These less dense films may not withstand the mechanical stress of subsequently performed integrated circuit fabrication processes such as chemical mechanical polishing (CMP) and packaging. That is, the films may crack or become crushed internally. In addition, these films tend to poorly adhere to other materials and may delaminate at interfaces with adjacent layers when subjected to the mechanical forces produced by CMP and other fabrication processes.

What are needed therefore are methods of improving the mechanical strength and adhesive properties of low-k dielectric films without substantially deleteriously affecting the desired properties of the low-k films.

SUMMARY

The present invention addresses this need by providing methods for improving the mechanical properties of a dielectric film on a partially fabricated integrated circuit while limiting shrinkage and limiting any increase in dielectric constant. Methods include (a) providing the partially fabricated integrated circuit having a low-k dielectric film formed thereon, (b) exposing the dielectric film to UV radiation of modulated intensity to thereby improve the mechanical properties of the dielectric film while limiting shrinkage and limiting any increases in dielectric constant and (c) forming one or more additional layers on the partially fabricated integrated circuit. The low-k dielectric film may be a porous or non-porous (sometimes referred as “dense”) dielectric film.

While the methods of the present invention can be employed to improve the mechanical properties of many different types of dielectric material in many different applications, much of this document will focus on carbon-doped silicon oxides (CDO) as the dielectric material. In other embodiments, silicon oxide may be doped with fluorine and/or other elements and even metals. Generally, the CDO films are comprised of carbon (typically in the form of methyl or other hydrocarbon groups) in addition to silicon and oxygen. A wide range of precursors is available to produce CDO films. These include various carbon containing compounds and silicon containing compounds. In many cases, a single precursor compound will include silicon, carbon, and sometimes oxygen.

In some cases the precursor film is formed by co-depositing the porogen with the structure former. The porogen is frequently, but not necessarily, an organic material and the structure former a silicon-containing material. As general examples, the structure former can be produced from silanes, alkylsilanes (e.g., trimethylsilane, di-tert-butylsilane and tetramethylsilane), alkoxysilanes (e.g., methyltriethoxysilane (MTEOS), methyltrimethoxysilane (MTMOS) diethoxymethylsilane (DEMS), methyldimethoxysilane (MDMOS), trimethylmethoxysilane (TMMOS) and dimethyldimethoxysilane (DMDMOS)), linear siloxanes, cyclic siloxanes (e.g. octamethylcyclotetrasiloxane (OMCTS) and tetramethylcyclotetrasiloxane (TMCTS)), silylalkenes (e.g., vinyltrimethylsilane (VTMS)), silylalkynes (e.g., trimethylsilylacetylene (TMSA), bis-trimethylsilylacetylene (BTMSA), or a combination thereof. One preferred class of porogen compounds is the polyfunctional cyclic non-aromatic compounds. Examples of such compounds are terpenines such as alpha terpenine (ATRP), norborenes such as 5-ethylidene-2-norbornene (ENB), limonene (C₂H₅OH) and other related compounds.

The dielectric may be of the “high density” variety (substantially pore free) or the “low density” variety (porous). The pores in porous films can be of many different sizes, ranging from nanometer scale to micron scale depending on the application. Regardless of its structure and composition, the material preferably has a relatively low dielectric constant (e.g., less than about 4, and more typically less than about 3) and relatively high mechanical strength. In many applications, the thickness of the dielectric film is between about 50 Angstroms and 5 micrometers and more preferably between about 500 Angstroms and 5,000 Angstroms.

Improvements of the mechanical properties of the dielectric film as a result of using methods of the invention include improvements in the hardness and stiffness of the film. The hardness of a nonporous film is preferably increased by about 0.3 GPa or greater and more preferably it is increased by about 0.7 GPa or greater (which corresponds to a increase in modulus of about 4.6 GPa or greater). The hardness of a porous film is preferably increased by about 0.9 Gpa or greater (which corresponds to a increase in modulus of about 5.0 GPa or greater).

In addition to improving the mechanical strength of the dielectric film, techniques described herein limit the film shrinkage and any increases in dielectric constant that may typically accompany UV exposure of dielectric films. In preferred embodiments, the dielectric non-porous film shrinks by no more than about 10% and the dielectric constant increases by no more than about 1% whereas a porous film will preferably shrink by no more than about 25% and more preferably by no more than about 15% and the dielectric constant increases by no more than about 8% and more preferably by no more than about 4%.

As indicated, the present invention involves exposing the dielectric film to a UV source that produces modulated or oscillating UV radiation at the substrate surface. The choices of UV wavelength(s), total exposure time and intensity, modulation period and amplitude, etc. depend on a number of factors, including the thickness of the dielectric film and the composition of the dielectric film. In some preferred embodiments, the oscillating UV radiation has a period of between about 1μ seconds and 5 minutes, and more preferably between about 1 millisecond and 30 seconds. The duty cycle of the UV source preferably ranges between about 1% and about 90%. The total exposure time to oscillating UV radiation is preferably between about 1 second and about 60 minutes. The amplitude (i.e., intensity variation) of the UV radiation will preferably vary between about 0 and 3 Watts/cm². Typical wavelengths used for CDO films range between about 150 nm and 800 nm.

The apparatus employed to implement the invention can have one or more UV sources. In some embodiments described herein, the apparatus will have a single UV source. The modulation may be introduced by any of many different mechanisms for controlling the UV radiation delivered to the work piece. Examples include controlling UV source power, controlling mechanical barriers (e.g., an aperture or rotating chopper) between the UV source and the substrate, and controlling an optical element (e.g., a filter, lens, or mirror) between the source and the substrate.

These and other features and advantages of the invention will be described in detail below with reference to the associated drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

The following detailed description can be more fully understood when considered in conjunction with the drawings in which:

FIG. 1 is a flowchart summarizing stages of example implementations of the invention.

FIG. 2 is a chart representing an example of modulated UV exposure as a function of time in accordance with the invention.

FIG. 3 is a chart representing film shrinkage as a function of UV exposure time using continuous and modulated UV exposure modes.

FIG. 4 is a chart representing film dielectric constant as a function of UV exposure time using continuous and modulated UV exposure modes.

FIG. 5 is a schematic representation of an UV apparatus suitable for film treatment in accordance with some embodiments of this invention.

DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT

The Dielectric Film

In the following description, numerous specific details are set forth in order to provide a thorough understanding of the present invention, which pertains to improving the mechanical strength of a low-k dielectric film by way of modulated UV exposure. The present invention may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail to not unnecessarily obscure the present invention. While the invention will be described in conjunction with the specific embodiments, it will be understood that it is not intended to limit the invention to the embodiments.

The present invention improves the dielectric film's mechanical properties with relatively minimal increase of k value and minimal film shrinkage. As used herein “semiconductor substrates” include any semiconductor substrate at any of the various states of manufacture/fabrication in the production of integrated circuits. Thus, the concept of a semiconductor substrate includes whole wafers and dies, partially fabricated integrated circuits and completely fabricated integrated circuits, whether or not packaged, and the like.

Many different types of low-k dielectric films may be processed using the present invention. This document will focus on carbon-doped silicon oxide (CDO) films. These can have various amounts of carbon (typically in the form of hydrocarbon groups such as methyl and/or methylene groups) depending upon desired film qualities and applications. Note, however, that methods of the invention are not limited to CDO films. For example, the methods may also be used to effectively strengthen silicon dioxide films containing other dopants such as fluorine or various metals. The invention may also extend to undoped silicon oxide films and even non-silicon dioxide based dielectric materials.

The present invention can be used on both porous and non-porous (sometimes referred to as “dense”) dielectric films. Any suitable method for forming a non-porous dielectric film may be used. One method involves PECVD methods using a silane, silane derivative, siloxane, siloxane derivative or a combination of two or more of these compounds. Methods of fabricating porous films typically involve forming a composite film (referred to herein as a “precursor film”) containing two components: a porogen (typically an organic material of low or high molecular weight (e.g., a polymer)) and a structure former or dielectric material (e.g., a silicon containing material). Once the precursor film is formed on the substrate, the porogen component is removed, leaving a structurally intact porous low-k dielectric matrix. Various porogens and porogen-removal techniques are described in U.S. patent application Ser. No. 10/800,377, previously incorporated by reference. Generally, a porogen is any removable material that defines void regions in a dielectric matrix. The porogen may be removed by thermal methods, treatment with plasma, supercritical extraction, UV-mediated techniques, electron beam treatment and the like.

The dielectric film (or precursor film in the case of a porous dielectric) may be formed by any of numerous techniques. Examples include spin-coating processes, print-on, dip coating, thermal process, supercritical deposition process, and chemical vapor deposition—particularly plasma enhanced chemical vapor deposition (PECVD). In one example, a methylsilsesquioxane film is formed using spin-on-glass techniques. In other examples, the film is deposited using standard CVD or PECVD methods in which organo-silane precursors such as methylsilanes are used with oxidizing agents such as oxygen, nitrous oxide or carbon dioxide, or an inert gas such as nitrogen, argon, helium, or a mixture of oxidizing gas and inert gas. A range of examples of precursors for the dielectric film (particularly for CVD processes) includes silane, alkylsilanes (e.g., trimethylsilane, di-tert-butylsilane, and tetramethylsilane), alkoxysilanes (e.g., tetraethoxysilane (TEOS), methyltriethoxysilane (MTEOS), methyltrimethoxysilane (MTMOS) diethoxymethylsilane (DEMS), methyldimethoxysilane (MDMOS), trimethylmethoxysilane (TMMOS) and dimethyldimethoxysilane (DMDMOS)), linear siloxanes and cyclic siloxanes (e.g. octamethylcyclotetrasiloxane (OMCTS) and tetramethylcyclotetrasiloxane (TMCTS)), silylalkenes (e.g., vinyltrimethylsilane (VTMS)), silylalkynes (e.g., trimethylsilylacetylene (TMSA), bis-trimethylsilylacetylene (BTMSA). Any suitable method may be used to deposit the dielectric film, including a PECVD method.

The thickness of the dielectric layer depends upon the ultimate application. As an example, the thickness may range between about 50 to 1500 angstroms for a hard mask application. For an interlayer dielectric or packaging application, the thickness may range up to about 2 to 3 microns. In some cases, extra thickness is required to provide some amount of sacrificial dielectric to accommodate a subsequent planarization or polishing step. In some cases, the thickness of the precursor layer may be driven in part by the ability of the UV radiation to penetrate the film and remove the porogen. Therefore, relatively thinner precursor layers may be required for some processes.

Methods of the invention involve improving 1) the “mechanical performance” of the porous low-k dielectric film, 2) with minimal k value increase, and 3) with minimal film shrinkage. Mechanical performance may be manifest in terms of hardness, modulus, intrinsic stress, etc. Hardness and modulus are well defined within the art and will not be discussed in detail herein. Measures of film hardness and modulus presented herein may be made with any suitable apparatus including nano-indenter device.

One way to characterize mechanical performance of a dielectric film is via a “cracking threshold” measurement. This is a measure of thickness of a dielectric film on a blank substrate (e.g., a flat 200 mm wafer) that can be deposited without forming a crack. In a typical experiment, the dielectric is deposited to various thicknesses using a single set of process conditions. The resulting wafer (with dielectric film) is set aside without disturbance for a period of time (e.g., one day) and then examined for cracks. The greatest thickness at which no crack is observed is the cracking threshold. For many processes, the cracking threshold is measured in micrometers.

The Modulated UV Source

As indicated, methods of the invention involve exposing a dielectric film to modulated UV radiation. It will be appreciated by those skilled in the art that the UV radiation used with the invention encompasses near-UV, far-UV, as well as UV wavelengths. Some films may be more effectively treated using UV light with particular ranges of wavelengths and/or intensities. In the present invention, the intensity of the UV radiation is modulated and typically oscillating. The modulated UV radiation can be achieved in any number of ways including providing a UV light source adapted to providing intermittent UV light intensities, providing more than one UV light source that can be turned on and off intermittently, shielding the substrate from UV exposure intermittently by using a shutter or light deflector (lens or mirror) for example, or moving the substrate intermittently in and out of the UV radiation exposure area. Some of these methods will be described herein.

Dielectric film exposure to UV radiation in general has been studied previously for various applications, including for porogen removal as well as mechanical strengthening applications. These applications of UV exposure are discussed, for example, in the previously referenced U.S. patent application Ser. No. 10/404,693, and U.S. patent application Ser. No. 10/800,377, both previously incorporated by reference. The present invention focuses on using modulated or oscillating UV exposure.

For context, FIG. 1 provides a flow chart depicting one general high-level process flow in accordance with some embodiments of the present invention. Initially, a dielectric film is provided on a substrate as indicated by a process block 101. As indicated, the thickness of the dielectric film will depend upon the ultimate application. It is worth noting that for identical compositions, porous films have lower dielectric constants than non-porous CDO films. For example, porous films typically have k values ranging between about 1.8 and 2.8 whereas non-porous CDO films typically have k values ranging between about 2.4 and 4.0. As described above, various techniques for forming a CDO film may be employed. It is noted again that the invention is not limited to any particular type of dielectric film or deposition method.

The dielectric film, provided at block 101, is exposed to modulated UV radiation, as indicated at block 103. As mentioned previously, the modulated UV radiation can be achieved using any of a number of techniques. In preferred embodiments, one UV radiation source, that is capable of providing modulated UV intensities, is used. An example of a suitable apparatus for the invention is described in further detail.

Returning to FIG. 1, after dielectric film is exposed to modulated UV radiation, additional layer(s) as required by the IC manufacturing process is/are formed over the dielectric film. See block 105. In some cases, the dielectric film is etched with vias and/or trenches before the additional layer(s) is/are deposited. After operation 105, the process flow of FIG. 1 is complete.

FIG. 2 is a graphical representation of UV exposure as a function of time in accordance with an example of the present invention. UV Intensity (y-axis) and Time (x-axis) are in arbitrary units. UV radiation reaching the substrate is modulated between Level 1 intensity and Level 2 intensity. Arbitrarily, Level 1 intensity is higher than Level 2 intensity. Substrate exposure to Level 1 intensity occurs periodically at intervals with particular time durations and exposure to Level 2 intensity occurs periodically at intervals with other time durations. As shown, the period of oscillation is given by time 201. In the depicted example, Level 1 phase is about twice the duration of Level 2 phase. If Level 2 intensity was zero (as would occur if the UV light source was turned OFF or blocked during Level 2 phases), the duty cycle of the UV light source would be 67% (i.e., ON two thirds of the time and OFF one third of the time). The graph of FIG. 2 shows four cycles of Level 1 exposures, but of course any number of cycles of exposures can be used as necessary to effect improvement in the dielectric layer's mechanical properties.

In a fabrication environment, various characteristics of the modulation may impact the process. These include the maximum and minimum intensity levels, the period of the modulation cycle, the duty cycle, the total exposure time. In preferred embodiments, the light intensity amplitude may be between about 1 μW/cm² and 3 W/cm². In a typical case, the minimum light intensity level is 0 (e.g., light source is turned OFF), although this is not necessary. The period of the modulation may be between about 1 μs seconds and 10 minutes, for example. For at least some CDO films, it has been found that a cycle period of between about 1 seconds and 30 seconds works well. The duty cycle (e.g., percentage of time the light source is ON) is preferably between about 1% and 90% and more preferably between 10% and 80%. The total time during which the dielectric film is exposed to the modulated UV radiation may be between about 1 second and 60 minutes, more preferably between about 30 seconds and 5 minutes. In some cases, it will be beneficial to control the number of modulation cycles as opposed to merely controlling the total exposure time. The UV wavelengths used can also vary, depending in part on the film composition and thickness. For certain CDO films, UV wavelengths between about 150 nm and 800 nm are used. Note that some UV sources will include a relatively wide spectral power distribution, with intensity peaks at multiple wavelengths. And if multiple UV sources are used, there will be, of course, multiple wavelengths. Also note that in some embodiments, the modulation characteristics may vary from cycle to cycle. For example, the amplitude, period, or duty cycle may vary from one cycle to the next in a defined or random mode.

The wafer substrate temperature may influence the hardening process. In some embodiments, higher temperatures may be more effective, but the temperature should not be too high as to cause damage to the substrate device. In general, temperatures below about 450 degrees C. are preferable, more preferably not greater than about 400 degrees C., as higher temperatures can damage a partially fabricated device, particularly one that employs copper lines. Typical temperatures range between about room temperature (i.e., 20 degrees C.) up to 450 degrees C. It should be noted that exposure to UV radiation can itself contribute to substrate heating.

As mentioned previously, low-k dielectric films treated with UV exposure result in films with improved mechanical properties (e.g., increased hardness and modulus). In preferred embodiments, the hardness of a non-porous film is increased by about 0.3 GPa or greater, and more preferably by about 0.7 GPa or greater (which corresponds to an improvement in modulus of about 4.6 GPa or greater) after modulated UV treatment in accordance with the invention. For a porous film, the hardness is increased by about 0.5 GPa or greater, and more preferably by about 0.9 GPa or greater (which corresponds to an improvement in modulus of about 5.0 GPa or greater) after modulated UV treatment in accordance with the invention.

In addition to improving the mechanical properties of the film, modulated UV exposure, as compared to continuous UV exposure, has fewer deleterious effects. Specifically, films exposed to modulated UV radiation experience less film shrinkage, less increase in dielectric constant, and higher mechanical strength. Examples showing advantages of the invention are presented in FIGS. 3 and 4 and described in the next section. In general, the dielectric film preferably will shrink by no more than about 25% (porous films), or no more than about 10% (non-porous films), after exposure to modulated UV radiation. Furthermore, the dielectric constant of the film preferably will increase by no more than about 8% (more preferably by no more than about 4%) for a porous film and by no more than about 1% for a non-porous film after such exposure.

EXAMPLES

As indicated above, it has been found that exposure to continuous UV radiation can cause unacceptable shrinkage of CDO dielectric films. In addition, it has been found exposing such dielectric films to continuous UV radiation typically increases the k value of these films. Although not wishing to be bound to theory, this is thought to be in part due to deleterious bond reconstruction within the film. Thus, until this invention there was often an unacceptable trade-off in exposing a dielectric film to UV radiation: enhanced mechanical strength coupled with too much shrinkage and dielectric constant or acceptable levels of shrinkage and dielectric constant increase coupled with unacceptable mechanical strength. Use of modulated UV radiation, in accordance with this invention, avoids this trade-off and produces dielectric films with good mechanical strength, limited shrinkage, and limited increase in dielectric constant.

FIG. 3 is a graph representing the percentage of film shrinkage (y-axis) as a function of time (x-axis) of films exposed to modulated UV radiation and unmodulated UV radiation. One film was exposed to only an unmodulated “Continuous Mode” UV exposure and another film was exposed to only a “Modulated Mode” UV exposure. The film shrinkage of each of the films was measured at different exposure times, as indicated by the data points. The labeled lines indicate the best-fit lines for the data points. Both films were non-porous CDO having thicknesses of about 5000 Angstroms and produced from TMCTS (1,3,5,7-tetramethylcyclotetrasiloxane) and carbon dioxide by PECVD.

The UV power at the surface of the 5,000 Angstrom CDO films was approximately 2 W/cm² at 100% intensity. The exposure was performed at a base pressure of 8 mTorr and at a temperature of about 100 Celsius in a vacuum chamber. The UV source provided radiation in the range of about 200 to 800 nm, with a peak near 380 nm. In the modulated mode, each cycle comprised 30 seconds of UV exposure at 100% intensity (level 1) followed by 30 seconds of no illumination (0% UV intensity—level 2). In one case, the cycle was repeated 3 times to achieve a total of 90 seconds UV exposure. In another case, the cycle was repeated 6 times to achieve a total of 180 seconds UV exposure.

As shown in FIG. 3, the film treated by Modulated Mode UV exposure experienced significantly less film shrinkage compared to the film treated with Continuous Mode UV exposure. Furthermore, the disparity in the amounts of shrinkage between the two films becomes greater with increasing UV exposure. For example, data point 301 shows that when the film exposed to Continuous Mode UV was exposed for about 60 seconds, it experienced about 4% film shrinkage. In comparison, data point 303 shows that when the film exposed to Modulated Mode UV was exposed for about 90 seconds, it experienced a little over 3% film shrinkage. As another example, data points 305 and 307 show film shrinkage percentages of films exposed to Continuous and Modulated UV, respectively. Both samples had UV exposure time of about 120 seconds. The film exposed to Continuous Mode UV (305) experienced about 10% shrinkage while the film exposed to Modulated Mode UV (307) experience only about 4%. At 180 seconds, the total shrinkage of the modulated mode film was only 5.5%. The film shrinkage was determined by calculating the difference in the thickness measured using a reflectometer or spectroscopic ellipsometer before and after the UV exposure.

It has been found that in addition to ameliorating the effects of thermal shrinkage, modulating the UV radiation can reduce any deleterious increase in the film's dielectric constant (k). This is shown, for example, by the graph of FIG. 4 representing the dielectric constant (y-axis), k, as a function of time (x-axis) of films treated with continuous and modulated UV exposure. As with the films in FIG. 3, both films were non-porous CDO produced from TMCTS (1,3,5,7-tetramethylcyclotetrasiloxane) and having thicknesses of about 5000 Angstroms each. Also, as with the data of FIG. 3, one film was exposed to Continuous Mode UV radiation and another was exposed to Modulated Mode UV radiation. The dielectric constant, k, of each of the films was measured at different exposure times, as indicated by the data points. The best-fit lines for the data points for each are indicated by the labeled lines. The dielectric constant, k was measured by using a SSM Mercury Probe.

As shown by FIG. 4, the films treated by Modulated Mode UV experienced less increase in k compared to the film treated by Continuous Mode UV. Specifically, the k value for the Continuous Mode UV exposed film increased to over 2.8 after about 120 seconds of exposure (see data point 401) while the k value for the Modulated Mode UV exposed film stayed well under 2.75 even after about 180 seconds of exposure (see data point 403).

For the modulated mode treatment, the following film properties were measured.

3 Cycles—Total of 90 Seconds Exposure

Thickness Shrinkage—3%

Shift in Dielectric Constant—0

Hardness—1.60 GPa

Modulus—10.7 GPa

Change in hardness (after treatment−before treatment)−0.32 GPa

Change in modulus (after treatment−before treatment)−2.0 GPa

6 Cycles—Total of 180 Seconds Exposure

Thickness Shrinkage—5.5%

Shift in Dielectric Constant—0

Hardness—1.97 GPa

Modulus—13.3 GPa

Change in hardness (after treatment−before treatment)−0.69 GPa

Change in modulus (after treatment−before treatment)−4.6 GPa

In addition to the data presented above for non-porous films, additional experiments with porous CDO films were also performed. Two different porous CDO samples prepared from diethoxymethylsilane (DEMS) and alpha-terpiene (ATRP). They were treated with continuous and modulated UV radiation having an intensity of about 2 Watts/cm². Prior to UV exposure, both films had k values of about 2.7 and hardness values of about 0.3 GPa. After exposure, the film exposed to continuous UV radiation (about 5 minutes) had a k value of about 2.25, a hardness value of about 1.2 GPa and experienced thermal shrinkage of about 21%. The film exposed to modulated UV radiation (10 cycles of 30 seconds ON and 30 seconds OFF) had a k value of about 2.25, hardness value of about 1.2 GPa and experienced thermal shrinkage of about 17%. Note that for these porous film samples the k values decreased after exposure to UV radiation. This is due to the fact that some porogen material was likely removed during UV exposure, resulting in a lowering of the measured k value.

Apparatus

The present invention can be implemented in many different types of apparatus. Generally, the apparatus will include one or more chambers (sometimes referred to as process vessels) that house one or more wafers (substrates) and are suitable for wafer processing. At least one chamber will include a UV source. A single chamber may be employed for all operations of the invention or separate chambers may be used. Each chamber may house one or more wafers for processing. The one or more chambers maintain the wafer in a defined position or positions (with or without motion within that position, e.g. rotation, vibration, or other agitation) during porogen removal and post porogen removal processes such as anneal, silanol capping and/or treatment with reactive gas plasma, if used. For certain operations in which the wafer is to be heated, the apparatus may include a heating platen.

FIG. 5 is a schematic diagram of an example chamber system in accordance with the invention. A substrate holder 501 and a UV light source 507 are housed within a chamber 500. In some embodiments, a quartz filter is placed between the substrate holder 501 and UV light source 507 (not shown). In alternate embodiments, the light source may be mounted outside the chamber on a window. Controller 513, which is typically a computer processor such as a PC or computer workstation, controls UV light source 507 according to a prescribed modulation regimen. Chamber 500 is capable of holding a vacuum and is connected with a vacuum pump 509 and gauge 511. Chamber 500 may also be connected to a series of vacuum pumps (not shown) to achieve a certain vacuum level. Air can be let back into chamber 500 after an evacuation using inlet valve 515. Chamber 500 may be one chamber in a multi-chambered system or it may be a stand-alone apparatus. Substrate holder 501 holds substrate 503 such that it can be irradiated with light from UV light source 507. Substrate holder 501 has a heater 505 that can heat the substrate to defined temperatures and can be controlled by a temperature controller (not shown).

UV light source 507 is a mercury vapor lamp or other source of UV radiation of the required characteristics; e.g., a laser (not shown), such as an Excimer laser, capable of providing sufficiently intense UV light. In cases where a laser is used, various optical elements may be required to direct the UV light toward portions of the substrate. Methods for directing the laser light at different portions of the substrate at different times may be required as well. In a specific embodiment, the UV source directs UV radiation on the substrate at an intensity of between about 1 μW/cm² and 10 W/cm² in the range of 200 to 400 nanometers.

During normal operation, chamber 500 is first evacuated using vacuum pump 509 to a desired vacuum level as measured by gauge 511. In some embodiments certain gas or mixture of gases are purged through the inlet valve 515 at a chosen flow while the chamber is under vacuum. Next, controller 513 modulates UV light source 507 in a periodic manner to irradiate substrate 503. For example, if a duty cycle of 50% with a period of 60 seconds is used, controller 513 may periodically turn UV light source ON for 30 seconds and then OFF for 30 seconds. After substrate 503 has been treated with modulated UV light for a sufficient amount of time, controller 513 turns UV light source OFF, chamber 500 is brought back to atmospheric pressure by flowing a gas through the inlet valve 515 and substrate 503 is removed from chamber 500.

In this example, it is presumed that controller 513 operates by controlling power to the light source. Other modulation control mechanisms may be employed as well. Some of these will be purely mechanical; e.g., moving irises, choppers, and the like. Others will be optical; e.g., varying lens, mirrors, filters, and the like.

Note that the apparatus depicted in FIG. 5 is only an example of a suitable apparatus and other apparatuses designed for other methods involved in previous and/or subsequent processes may be used. For example, methods of the invention may be used with a standard PECVD chamber used to deposit the precursor layer if the chamber is equipped with a UV radiation source. Some supercritical fluid chamber systems may also be configured to include a UV radiation source. Some systems may also be used to perform the various operations of a porogen film process such as post-porogen removal anneal and/or silanol capping procedures and/or plasma treatment. Obviously, in cases where different types of operations are used, the chamber system will be configured with inlet valves for letting in processes gases and the chamber will likely be pumped out between each of the operations.

While this invention has been described in terms of several embodiments, there are alterations, modifications, permutations, and substitute equivalents, which fall within the scope of this invention. It should also be noted that there are many alternative ways of implementing the methods and apparatuses of the present invention. It is therefore intended that the following appended claims be interpreted as including all such alterations, modifications, permutations, and substitute equivalents as fall within the true spirit and scope of the present invention. The use of the singular in the claims does not mean “only one,” but rather “one or more,” unless otherwise stated in the claims. 

What is claimed is:
 1. A method of processing a partially fabricated integrated circuit substrate, comprising curing a dielectric layer of the partially fabricated integrated circuit substrate with modulated ultraviolet curing radiation, wherein curing the dielectric layer comprises exposing the dielectric layer to multiple cycles of modulated ultraviolet radiation, wherein each cycle of modulated ultraviolet radiation includes: (a) exposing the dielectric layer to ultraviolet radiation during a first time increment, and (b) exposing the dielectric layer to ultraviolet radiation during a second time increment, wherein at least one of wavelength and spectral distribution of the ultraviolet radiation is varied from (a) to (b).
 2. The method of claim 1, further comprising transitioning from (a) to (b) by moving the substrate out of and then into ultraviolet radiation exposure areas.
 3. The method of claim 1, wherein the wavelength is varied from (a) to (b).
 4. The method of claim 1, wherein the spectral distribution is varied from (a) to (b).
 5. The method of claim 1, wherein the modulated ultraviolet curing radiation further modulates duration of exposure.
 6. The method of claim 1, wherein the dielectric layer is an inter-level or inter-metal dielectric layer of the partially fabricated integrated circuit substrate.
 7. The method of claim 1, wherein the dielectric layer is a hardmask.
 8. The method of claim 1, wherein the dielectric layer is a packaging layer.
 9. The method of claim 1, wherein the dielectric layer is a silicon oxide layer.
 10. The method of claim 9, wherein the silicon oxide layer is a carbon-doped silicon oxide layer.
 11. A method of processing a dielectric layer on a substrate, said method comprising curing the dielectric layer with modulated ultraviolet curing radiation, wherein the curing the dielectric layer with the modulated ultraviolet curing radiation comprises exposing the dielectric layer on the substrate to at least two cycles of ultraviolet curing radiation and wherein at least one of wavelength and spectral distribution of the ultraviolet radiation are varied within each cycle and wherein the dielectric layer is part of a partially fabricated integrated circuit substrate.
 12. The method of claim 11, wherein the dielectric layer comprises silicon.
 13. The method of claim 11, wherein the dielectric layer shrinks by less than 25%, and a dielectric constant of the dielectric layer changes by less than 8%.
 14. The method of claim 11, wherein curing the dielectric layer comprises moving the substrate into and out of ultraviolet radiation exposure areas.
 15. The method of claim 11, wherein the dielectric layer is an inter-level or inter-metal dielectric layer of the partially fabricated integrated circuit substrate.
 16. The method of claim 11, wherein the dielectric layer is a hardmask or packaging layer.
 17. The method of claim 11, wherein the dielectric layer is a packaging layer.
 18. The method of claim 11, wherein the dielectric layer is a silicon oxide layer. 